Papua New Guinea Thickness 0.5-2.0mm Anti-Seepage Double-Sided Smooth HDPE Geomembrane for Tailing Dam Liners

Smooth HDPE Geomembrane is manufactured from High Density Polyethylene resin with proportional carbon black antioxidant, anti-aging and UV-resistance materials by the technology of coextrusion-blown triple layer.

Category:

Papua New GuineaSmooth HDPE Geomembrane

Phone:+86 13105487610

Product Description

Introduction

Glossy HDPE geomembrane is a geomembrane product with a easy floor on each sides. It is made of excessive best excessive density polyethylene material, which is made of a aggregate of about 97.5% polyethylene, 2.5% carbon black, a hint quantity of antioxidant and warmness stabilizer. The resin used in the manufacturing manner is particularly designed for geomembrane. Applied uncooked polyethylene resin uncooked substances

Video Showcase

Applications

1. Environmental protection, waste landfills, sewage treatment, poisonous and hazardous substance disposal sites, unsafe items warehouses, industrial waste, development and blasting waste, etc.

2. Water conservancy, such as seepage prevention, plugging, reinforcement of rivers, lakes, reservoirs and dams, seepage prevention of canals, vertical core walls, slope protection, etc.

3. Gardens, synthetic lakes, ponds, golf direction pond backside lining, slope protection, etc.

4. Mining industry, seepage prevention of the backside lining of washing tank, heap leaching tank, ash dump, dissolution tank, sedimentation tank, storage yard, tailing pond, etc.

5. Aquaculture (fish pond, shrimp pond lining, sea cucumber ring protection, and so forth

Working Drawing

Specifications

❶ Thickness: 0.2mm-3.0mm

❷ Width:1-10m

❸ Colour: black, green, blue, yellow

Properties	Test Method	GMSH050	GMSH075	GMSH100	GMSH150	GMSH200
Thickness	ASTM D5199	0.50 mm	0.75 mm	1.00 mm	1.50 mm	2.00 mm
Density	ASTM D1505	0.940 g/co	0.940 g/cc	0.940 g/cc	0.940 q/cc	0.940 g/cc
Tensile Properties
Yield strength	ASTM D6693	7kN/m	11 kN/m	15 kN/m	22 kN/m	29kN/m
Break strength	Type IV	13 kN/m	20 kN/m	27 kN/m	40 kN/m	53 kN/m
Yield elongation		12%	12%	12%	12%	12%
Break elongation		700%	700%	700%	700%	700%
Tear Resistance	ASTM D1004	62 N	93 N	125 N	187 N	249 N
Puncture Resistance	ASTM D4833	160 N	240 N	320 N	480 N	640 N
Stress Crack Resistance	ASTM D5397	500 hrs	500 hrs	500 hrs	500 hrs	500 hrs
m Carbon Black Content	ASTM D1603	2.0%	2.0%	2.0%	2.0%	2.0%
Carbon Black Dispersion	ASTM D5596	For 10 different views:9in Categoriesor 2 and 1 inCategory 3
Oxidative Induction Time (OIT	ASTM D3895	100 min.	100 min.	100 min.	100 min.	100 min.
UV Resistance High Pressure OIT retained after 1600hrs	ASTM D5885	50%	50%	50%	50%	50%
Dimensions
Roll Width (m)		7	7	7	7	7
Roll Length (m		420	280	210	140	105