Papua New Guinea Factory Supply Tank Fish Farming Pond Liner Geomembrane 1.5 mm

Smooth HDPE Geomembrane is manufactured from High Density Polyethylene resin with proportional carbon black antioxidant, anti-aging and UV-resistance materials by the technology of coextrusion-blown triple layer.

Category:

Papua New GuineaSmooth HDPE Geomembrane

Phone:+86 13105487610

Product Description

Introduction

High Density Polyethylene (HDPE) is the excessive density model of PE plastic and is more difficult and denser than the LDPE, however is much less ductile, and lighter than water. Climax HDPE Film / Sheet / Liner / Geomembrane has proved to be a boon specifically for creating international locations like India with the aid of taking part in an essential function to forestall the air and groundwater pollution. The fantastic issue is that it can be without problems moulded and welded collectively and the use of UV Stabilizers improves its climate resistance. High Density Polyethylene Geomembrane lives up to the expectations which are demanded in modern world of environmental engineering. Climax HDPE's top intent is to hold the Nature clean.

Video Showcase

Applications

1.Set seepage prevention and drainage features in one, with isolation and reinforcement functions.
2.High composite strength, excessive peel strength, excessive puncture resistance.
3.Strong drainage capacity, massive friction coefficient, small linear enlargement coefficient.
4.Good getting old resistance, broad temperature range, secure quality.

Working Drawing

Specifications

❶ Thickness: 0.2mm-3.0mm

❷ Width:1-10m

❸ Colour: black, green, blue, yellow

Properties	Test Method	GMSH050	GMSH075	GMSH100	GMSH150	GMSH200
Thickness	ASTM D5199	0.50 mm	0.75 mm	1.00 mm	1.50 mm	2.00 mm
Density	ASTM D1505	0.940 g/co	0.940 g/cc	0.940 g/cc	0.940 q/cc	0.940 g/cc
Tensile Properties
Yield strength	ASTM D6693	7kN/m	11 kN/m	15 kN/m	22 kN/m	29kN/m
Break strength	Type IV	13 kN/m	20 kN/m	27 kN/m	40 kN/m	53 kN/m
Yield elongation		12%	12%	12%	12%	12%
Break elongation		700%	700%	700%	700%	700%
Tear Resistance	ASTM D1004	62 N	93 N	125 N	187 N	249 N
Puncture Resistance	ASTM D4833	160 N	240 N	320 N	480 N	640 N
Stress Crack Resistance	ASTM D5397	500 hrs	500 hrs	500 hrs	500 hrs	500 hrs
m Carbon Black Content	ASTM D1603	2.0%	2.0%	2.0%	2.0%	2.0%
Carbon Black Dispersion	ASTM D5596	For 10 different views:9in Categoriesor 2 and 1 inCategory 3
Oxidative Induction Time (OIT	ASTM D3895	100 min.	100 min.	100 min.	100 min.	100 min.
UV Resistance High Pressure OIT retained after 1600hrs	ASTM D5885	50%	50%	50%	50%	50%
Dimensions
Roll Width (m)		7	7	7	7	7
Roll Length (m		420	280	210	140	105