1mm Smooth Surface HDPE Geomembrane for Construction Reservoir Engineering

Smooth HDPE Geomembrane is manufactured from High Density Polyethylene resin with proportional carbon black antioxidant, anti-aging and UV-resistance materials by the technology of coextrusion-blown triple layer.

Commodity name： 1mm Smooth Surface HDPE Geomembrane for Construction Reservoir Engineering

Category:

Smooth HDPE Geomembrane

Email:

john@xiuhegeo.com

Online consultation

Back to list

Description

Introduction

Our excessive density polyethylene (HDPE) geomembranes supply an impermeable barrier towards a large vary of solids and liquids. They showcase tremendous chemical and UV resistance,impermeability, and excessive yield and welded seam strengths, which is extensively used as the liner.(model in accordance to the thickness of distinction, distinct thickness and exclusive price) manufacturing capacity: thickness:0.1 mm -6 mm, width: 1-8 meters. It is appropriate for seepage manipulate in unique industries, and is broadly used for aquaculture, seepage control, reservoirs or sewage remedy ponds.

Video Showcase

Applications

1. Good flexibility and excessive anti-seepage coefficient
2. Good warmness and bloodless resistance, with a large temperature vary for use (-70C~110C);
3. Good chemical stability, robust acid and alkali resistance, robust corrosion resistance:
4. It has sturdy climate resistance and great anti-aging performance
5. High tensile power and fracture elongation indicators, sturdy stress force, appropriate for use in a variety of harsh geological and climatic conditions, specifically appropriate for engineering in geological uneven agreement areas

Working Drawing

Specifications

❶ Thickness: 0.2mm-3.0mm

❷ Width:1-10m

❸ Colour: black, green, blue, yellow

Properties	Test Method	GMSH050	GMSH075	GMSH100	GMSH150	GMSH200
Thickness	ASTM D5199	0.50 mm	0.75 mm	1.00 mm	1.50 mm	2.00 mm
Density	ASTM D1505	0.940 g/co	0.940 g/cc	0.940 g/cc	0.940 q/cc	0.940 g/cc
Tensile Properties
Yield strength	ASTM D6693	7kN/m	11 kN/m	15 kN/m	22 kN/m	29kN/m
Break strength	Type IV	13 kN/m	20 kN/m	27 kN/m	40 kN/m	53 kN/m
Yield elongation		12%	12%	12%	12%	12%
Break elongation		700%	700%	700%	700%	700%
Tear Resistance	ASTM D1004	62 N	93 N	125 N	187 N	249 N
Puncture Resistance	ASTM D4833	160 N	240 N	320 N	480 N	640 N
Stress Crack Resistance	ASTM D5397	500 hrs	500 hrs	500 hrs	500 hrs	500 hrs
m Carbon Black Content	ASTM D1603	2.0%	2.0%	2.0%	2.0%	2.0%
Carbon Black Dispersion	ASTM D5596	For 10 different views:9in Categoriesor 2 and 1 inCategory 3
Oxidative Induction Time (OIT	ASTM D3895	100 min.	100 min.	100 min.	100 min.	100 min.
UV Resistance High Pressure OIT retained after 1600hrs	ASTM D5885	50%	50%	50%	50%	50%
Dimensions
Roll Width (m)		7	7	7	7	7
Roll Length (m		420	280	210	140	105